The Titan Bond Work Index Rod Mill is one-piece cast construction with integral wave liners of a form described by Bond. This mill is used to perform the necessary metallurgical testing to determine the grinding characteristics of ores and power requirements for operating production-size rod mills.

Bond Rod Mill Grindability Test Grinding Solutions can carry out Bond Rod Mill Work Index tests to determine the energy requirements for milling ore in a rod mill. The test requires a minimum of 20kg of -12.5mm material. Closing screen sizes typically range from 4.75mm to 212µm.

ENGR 3116 Mineral Processing 1 BOND WORK INDEX CALCULATIONS Assignment # 1 Due Friday, Sept. 16 th, 2016 1. A 1 kg. sample of a new ore was ground for 10 minutes in a laboratory rod mill with a 22 kg charge of rods of varying diameters from 5 to 12 mm. The 80 percent passing size of the sample before grinding was 1.3 mm while after grinding it was 127 microns.

To calculate Bond rod-mill work indices, the four samples were screened and the particle size distributions plotted in Fig. 2.The plot was used to find F 80 of the samples for calculations. Fig. 3, Fig. 4 show the grinding kinetics of Pb, Cu, Fe, and Mn ores in the Bond rod-mill in different test-sieves. The slopes of all lines in the figures are equal to the k value of Eq.

The Bond rod mill work index is not as common as the Bond ball mill work index, and there are two different variations on the mill apparatus.The SAGMILLING models expect a mill with a "wave liner", and is not compatible with mills using "smooth liners".

Bond ball mill work index, bwi, kwh/t 13.4 bond rod mill work index, rwi, kwh/t 18.1 table 1. example of ag/sag ball mill circuit wio calculations [1] [2] abstract optimum use of power in grinding, both in terms of grinding efficiency and use of installed capital, can.

Essa® Bond Test-Work Equipment. Internationally accepted mineral metallurgical standard test procedures to determine the physical properties of ores include the Bond ball mill work index and the Bond rod mill work index. These are empirical indices determined by close circuit grindability tests developed by F.C.Bond in the mid 1930's.

Using the Bond work index to measure operating comminution efficiency Download PDF. Download PDF. Published: 01 ... "Selection of rod mills, ball mills, pebble mills, and regrind mills," in Design and Installation of Comminution Circuits, Andrew L. Mular and Gerald V. Jergensen, eds., SME, Chapter 23, pp. 393–438.

Generally, Bond work index is a common method for selecting comminution equipment as well as estimation of grinding efficiency and calculating required power. In the current research, a simple, fast and accurate procedure is introduced to find the rod-mill work index based on …

The bond rod mill work index is a measure of the resistance of the material to grinding in a rod mill it can be used to determine the grinding power required for a given throughput of material under rod mill grinding conditions it is a locked cycle test conducted in closed circuit with a laboratory screen.

The Bond rod mill work index is not as common as the Bond ball mill work index, and there are two different variations on the mill apparatus.The SAGMILLING models expect a mill with a "wave liner", and is not compatible with mills using "smooth liners".According to the Bond standard procedure, the work index is determined by simulating a dry grinding in a closed circuit in the Bond ball ...

Measuring ore grindability in rod mills. The Bond Rod Mill Work Index is a measure of the resistance of the material to grinding in a rod mill. It can be used to determine the grinding power required for a given throughput of material under rod mill grinding conditions.

how to calculate mill bond or work index. An ore fed to a rod mill has a bond work index of 14.0 kwhrt-1.The p80 of feed to the mill averages 2.50 centimetres and the p80 of the product from the mill is 0.104 millimetres.A calculate the work required to grind the ore to the product size.B calculate the reduction ratio. →

The Bond's standard ball mill is used to determine the work index value of differ ent samples. The Bond work index is defined as the kilowatt-hours per short ton required to break from infinite size to a product size of 80% passing 100 µm. If the breakage characteristics of a material remain constant over all size ranges, the calcul ated work ...

The Bond Index conforming rod charge consists of: 6 rods of 1.25" diameter and 21" length. 2 rods of 1.75" diameter and 21" length. The grinding jar for the Bond Index Rod Mill is 12″ x 24″ in size and has a wave-shaped design. At least 15 to 20 kg sample material is required to simulate a closed grinding circuit in a ball or rod mill.

The mill power is = 22.5 Watts, calculated by (6). Fi- P nally the product is wet screened to find the size d80. 2.4. Rod Mill Semi Continuous Process The same mill is used for the semi continuous grinding tests which is similar to the Bond test but with the exist- ing …

The Bond ball mill work index test is thought to be additive because of its units of energy; nevertheless, experimental blending results show a non-additive behavior. [18] The SPI(R) value is known not to be an additive parameter, however errors introduced by block kriging are not thought to be significant .

specification of the Bond mill are given in Table 1. Table 1. Bond's mill specification and grinding conditions Mill diameter, D m, cm 30.48 Mill Length, L m, cm 30.48 Number of mill rotations in minutes, n, min-1 70 Mill balls weight, M b, kg 21.125 Geometry of mill liner smooth Grinding type dry V ore, cm 3 …

Bond Ball Mill Work Index, BWi, kWh/t 13.4 Bond Rod Mill Work Index, RWi, kWh/t 18.1 Table 1. Example of AG/SAG Ball Mill Circuit Wio Calculations [1] [2] ABstrAct Optimum use of power in grinding, both in terms of grinding efficiency and use of installed capital, can have a large effect on profitability.

Bond Rod Mill Work Index Equipment & Apparatus Review - Mineral . Mar 19, 2017 . 1 Introduction 2 Rocking of the laboratory mill 3 Issues with a smooth liner . Commentary on the apparatus of the Bond rod mill work index.

Bond's approach consists of determining the ore hardness characteristics, or Work Index (Wi) via standardized laboratory testwork. The full suite of Bond comminution tests provide the Ball Mill Work Index (BWi), the Rod Mill Work Index (RWi), the Crusher Work …

determination of the work index for ball and rod mills in 1952 and modified it in 1961. The standard Bond ball mill grindability test is a closed circuit dry grinding test with a 250% circulating load. The standard procedural outline of the test is stated in (Bond) 1961. The work index for a ball mill, Wi, is then calculated from the following ...

Bond Work Index for Rod Mill. Product Image. Introduction. The Bond Work Index for Ball Mill is a special equipment for testing Bond ball mill work index. Simple lab test can choose ball mill by power method or judge the effects of material properties change to the ball milling process or the operation condition of crusher by using this ...

Bond Work Index an overview ScienceDirect Topics. The rod mill work index laboratory test is conducted by grinding an ore sample prepared to 80% passing 12.7 mm (½ inch, the original test being developed in imperial units) to a product size of approximately 1 mm (in the original and still the standard, 14 mesh; see Chapter 4 for definition of mesh), thus determining the rod mill work index ...

A Bond rod mill work index test (BRMWI) is a standard test for determining the rod mill work index of an ore sample [21]. The BRMWI is a measure of the resistance of the material to crushing and grinding in a rod mill and is used to calculate the grinding power needed for a given material parcel regarding rod mill grinding conditions. Along ...

However, Bond Work Indeces are related to the type of equipment to be used (rod mill, ball mill, SAG uses Drop Ball parameter-Kwhr/m3-, so it is …

Commentary on the apparatus of the Bond rod mill work. Apr 27, 2016 rod milling, is fitted to a tumbling test, referred to as the Bond rod mill work index WiRM, or RWi. The apparatus used to determine this work index was described in 1943 by Bond amp Maxton and a slightly different apparatus was described by Bergstrom in 1985.

Bond Work Index an overview ScienceDirect Topics. The Bond work index is not solely a material constant but is influenced by the grinding conditions For example, the finer the grind size desired, the higher is the kWh/t required to grind to that size Magdalinovic [38] measured the Bond work index of three ore types using different test screen sizes He produced a correlation between the mass of ...

Bond Test WI's (kWh/t): Rod Mill: Ball Mill: 9.5 kWh/t.8 9 kWh/t . Bond Standard Circuit Work Index: Assume the rod mill Work Index of 9.5 applies from the actual rod mill feed sizeof 19,300 mµ (although some of this work might ideally be done by crushers to achieve a rod mill F80 of 16,000 m) to a rod µ

Essa® Laboratory Rod Mills. Essa manufactures a range of metallurgical laboratory size ball and rod mills to suit most applications. Included in the range is a Bond Index Mill, which has specific application in establishing the grindability of ores. The ball and the rod mill are of essentially the same basic concept comprising a barrel mounted ...